TPU|德国巴斯夫|1175A10W

用 途:
汽车配件,医疗器械,工业配件,电线电缆,鞋材薄膜,涂料胶粘剂
价 格:
标注的价格为:发布时期的那一段时间的价格,实时价格请电话咨询
备 注:
阻燃增韧级,属特殊品级,主要用于电线电揽等材料
优惠价:¥55 关注热度:
热线电话:158-9996-3239(李R)  138-2726-8341(杨R)
  • BASF Elastollan® 1175A10W Wire & Cable Grade Polyurethane Elastomer 物性表
    物理性能 额定值 (公制) 额定值 (英制) 测试方法
    密度 1.14 g/cc
    @Thickness 2.00 mm
    0.0412 lb/in³
    @Thickness 0.0787 in
    molded plaque, cured 20 hr at 100°C; ASTM D792
    机械性能 额定值 (公制) 额定值 (英制) 测试方法
    肖氏硬度 (邵氏 A) 75
    @Thickness 2.00 mm
    75
    @Thickness 0.0787 in
    molded plaque, cured 20 hr at 100°C; ASTM D2240
    极限抗拉强度 41.0 MPa
    @Thickness 2.00 mm
    5950 psi
    @Thickness 0.0787 in
    molded plaque, cured 20 hr at 100°C; ASTM D412
    抗张强度(屈服) 4.80 MPa
    @Strain 100 %
    696 psi
    @Strain 100 %
    ASTM D-412
      11.0 MPa
    @Strain 300 %
    1600 psi
    @Strain 300 %
    0.76 mm (0.030 in) extruded sheet; ASTM D-412
    伸长率 (断裂) 685 % 685 % on 0.030 in extruded sheet; ASTM D-412
    弯曲模量 0.0250 GPa
    @Thickness 2.00 mm
    3.63 ksi
    @Thickness 0.0787 in
    molded plaque, cured 20 hr at 100°C; ASTM D790
    撕裂强度 27.0 kN/m
    @Thickness 0.760 mm
    154 pli
    @Thickness 0.0299 in
    Split tear strength; extruded sheet; ASTM D-1938
    Graves Tear Strength 57.0 kN/m
    @Thickness 0.762 mm
    325 pli
    @Thickness 0.0300 in
    extruded sheet; ASTM D624
    泰伯磨损,毫克/1000次 20
    @Thickness 2.00 mm
    20
    @Thickness 0.0787 in
    H-18 wheel; ASTM D-1044; molded plaque, cured 20 hr at 100°C.
    永久压缩 25 % 25 % 22 hr at 23°C per ASTM D-395; 2.0 mm (0.080 in) molded plaque, cured 20 hr at 100°C.
      45 %
    @Temperature 70.0 °C
    45 %
    @Temperature 158 °F
    22 hr @ 70°C; ASTM D-395; 0.080 in molded plaque after curing 20 hrs at 100°C.
    Tensile Set 32 % 32 % at 200% elongation per ASTM D-412 is on 0.030 in extruded sheet.
    热性能 额定值 (公制) 额定值 (英制) 测试方法
    维卡软化温度 80.0 °C
    @Thickness 2.00 mm
    176 °F
    @Thickness 0.0787 in
    molded plaque, cured 20 hr at 100°C.; ASTM D1525
    玻璃化转变温度,Tg -47.0 °C -52.6 °F Pellet sample
    可燃性(UL94) V-2
    @Thickness 1.59 mm
    V-2
    @Thickness 0.0626 in
    Color: NC
      V-2
    @Thickness 3.14 mm
    V-2
    @Thickness 0.124 in
    Color: NC
      V-0
    @Thickness 0.900 mm
    V-0
    @Thickness 0.0354 in
    Color: NC